您所在的位置:網站首頁 > > 產品中心 > 通用PVC材料 > PVC特種料環保型90℃聚氯乙烯耐油阻燃柔軟護套料 W-9021H
環保型90℃聚氯乙烯耐油阻燃柔軟護套料 W-9021H
90℃Soft Lead-free Oil-resistant Flame-retardant PVC Jacketing Compound...
型號:0

參考價:¥

說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
Product Description產品描述
90℃soft lead-free oil-resistant flame-retardant PVC jacketing compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer, high-efficiency flame-retardant and other accessory ingredients.
環保型90℃聚氯乙烯耐油阻燃柔軟護套料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑、高效阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
 
Characteristics and Application 特點及用途
The products have excellent oil-resistant properties, flame-retardant property, soft and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of 90℃cables which have flame-retardant and oil-resistant property requirements.
產品具有良好的耐油性、阻燃性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于90℃耐溫等級并有阻燃和高耐油要求的電線電纜護套。
 
Processing Indicator加工工藝
Recommend to use single-screw extruders with L/D= 20-25.
建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
Model
牌號
Machine Barrel Temperature
機筒溫度
Molding Temperature
機頭溫度
W-9021H 150-175℃ 170-185℃
 

Physical and Electrical Properties
機械物理性能及電性能指標

Item

試驗項目

Unit
單位
Technical Requirements
技術要求
Density
比重
\ ≤1.40
Tensile Strength
拉伸強度
MPa ≥10.3
Elongation at Break
斷裂伸長率
% ≥150
Hardness
硬度
Shore A 70±5
200℃Thermal Stability
200℃時熱穩定時間
min ≥240
20℃Volume Resistivity
20℃時體積電阻率
Ω.m ≥1×108
Brittle Temperature with Impact
沖擊脆化溫度
-15
Oxygen Index
氧指數
  ≥27
Thermal Deformation
熱變形(90℃×6h)
% ≤50
Thermal Aging
熱老化試驗
\ 135℃×336h
Variation of tensile strength after aging
老化后拉伸強度變化率
% ±25
Elongation at break after changing the aging rate
老化后斷裂伸長率變化率
% ±25
Oil Resistance
耐油性能(ASTM 902)
(90℃×168h)
Tensile Strength Variation
拉伸強度變化率
% ±30
Elongation Variation
斷裂伸長率變化率
% ±30